Content pf Ferro Niobuim
|
Grade |
composition ％ | |||||||||||||||
| Nb | Ta | Al | Si | C | S | P | W | Ti | Cu | Mn | As | Sn | Sb | Pb | Bi | |
| ≤ | ||||||||||||||||
| FeNb70 | 70-80 | 0.8 | 3.8 | 1.5 | 0.04 | 0.03 | 0.04 | 0.3 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60—A | 60-70 | 0.5 | 2.0 | 0.4 | 0.04 | 0.02 | 0.02 | 0.2 | 0.2 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb60—B | 60-70 | 0.8 | 2.0 | 1.0 | 0.05 | 0.03 | 0.05 | 0.2 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50—A | 50-60 | 0.8 | 2.0 | 1.2 | 0.05 | 0.03 | 0.05 | 0.1 | 0.3 | 0.3 | 0.3 | 0.005 | 0.002 | 0.002 | 0.002 | 0.002 |
| FeNb50—B | 50-60 | 1.5 | 2.0 | 4.0 | 0.05 | 0.03 | 0.05 | |||||||||
Ferro Niobium is an added substance to the generation procedure of indistinct metals and will bestow a few alluring properties upon the subsequent compound. One of the essential advantages of adding Ferro Niobium to an amalgam is in its enemy of destructive properties (superior to anything carbon steel). Furthermore, the adding of Ferro Niobium to a combination can make it increasingly weldable and a lot more grounded. With the expansion of different components, for example, Zirconium, Ferro Niobium-created steel is ideal for directionally delicate applications, for example, suspension spans. Ferro Niobium expands high temperature opposition, consumption obstruction, oxidation obstruction, creep opposition, just as decreasing disintegration at higher temperatures.
ZHEN AN INTERNATIONAL CO., LTD
Mobile: +86-18211636583(whatsapp/wechat)
Fax: +86-372-5055180
Email:kay@zaferroalloy.com
Website: https://www.zaferroalloy.cn/
Head office: Huafu Office, Anyang City, Henan Province, China